Martensitic Stainless Steel 420, 2Cr13

420 stainless steel is a martensitic higher carbon version of types 410 and 416 stainless that can be hardened by heat treatment. It contains a minimum of 12 percent chromium, sufficient to give 420 corrosion resistance properties. It has good ductility in the annealed condition but is capable of being hardened up to 50 RHC. Its best corrosion resistance is achieved when 420 is hardened and surface ground or polished. In the hardened condition, 420 has good corrosion resistance to the atmosphere, foods, fresh water, mild alkalies and acids, steam, sterilizing solutions, crude oil, gasoline, and other similar corrosive media. The higher carbon content employed in 420 gives higher strength and hardness over stainless grades 410 and 416. In the annealed condition, 420 is relatively easy to machine, but if hardened to above 30 HRC, machining becomes more difficult. Fabrication must be by methods allowing for poor weldability and usually allow for a final harden and temper heat treatment. 420 is not recommended for use in temperatures above the relevant tempering temperature, because of reduction in mechanical properties. The scaling temperature is approximately 650°F.

Applications

420 stainless is widely used in the medical and cutlery industries. It is suitable for applications such as instruments, knives, hand tools, pump shafts and plastic moulds. 420 is not recommended for use in temperatures above the relevant tempering temperature, because of the reduction in mechanical properties.

Corrosion Resistance

Best corrosion resistance of 420 stainless is achieved when 420 is hardened and surface ground or polished. In the hardened condition 420 has good corrosion resistance to atmosphere, foods, fresh water, mild alkalis and acids, steam, crude oil and other similar corrosive media. 

Hardening

420 is suitable for heat treatment up to 52 HRc or higher depending on the carbon content and size of the component. European grade 1.2083 is a high carbon type 420 stainless and is ideally suited for application where highest achievable hardness is required. 

Form of Supply

main sizes ass hot rolled Thk 4.0--60mm x Width 20--350mm

Cold Rolled Thk 0.3--6.0 x Width 20--350mm